Mechanical Strength Analysis of Composite Boards Made from Sengon Buto (Enterolobium Cyclorobium)
Abstract
The amount of sawdust in sengon is abundant, so it is necessary to reduce the proportion of sawdust in sengon. This research aims to utilize sawdust and bark of buto sengon. The research was carried out experimentally, where variations in particle size were mixed with adhesive and given a pressure of 1 ton. Mechanical test is carried out by giving a loading of 50; 100; and 150 grams. The test results show that the use of sengon bark powder provides a better load-bearing ability than sengon stems.
References
Zulkarnaen and S. Mariani, “Pengaruh Penambahan Serbuk Gergaji Kayu Sengon Terhadap Kuat Tekan Dan Daya Serap Air Pada Paving Block,” Jurnal Saintek Unsa, vol. 1, no. September, pp. 162–169, 2016.
S. Slamet, “Karakterisasi komposit dari serbuk gergaji kayu (sawdust) dengan proses hotpress sebagai bahan baku papan partikel,” Prosiding SNST, vol. 1, no. 1, pp. 1–9, 2013.
A. F. R. Putra, E. Wardenaar, and H. Husni, “Andi Ferry Ramadhan Putra, Evy Wardenaar, Harnani Husni,” Jurnal Hutan Lestari, vol. 6, pp. 83–89, 2018.
A. Azhari, S. Falah, L. Nurjannah, S. Suryani, and M. Bintang, “Delignifikasi Batang Kayu Sengon oleh Trametes versicolor,” Current Biochemistry, vol. 1, no. 1, pp. 1–10, 2014, doi: 10.29244/cb.1.1.1-10.
I. Lessy, S. Ohorella, and S. Karepesina, “Sifat Fisis Kayu Sengon (Paraserianthes falcataria L. Nielsen) pada Lahan Agroforestry di Ambon, Maluku,” Jurnal Agrohut, vol. 9, no. 1, pp. 1–11, 2018.
dan S. Muhammad Hidayatulah, Yudi Firmanul Arifin, “Teknik Skarifikasi Percepatan dan Peningkatan daya Kecambah Benih Sengon Buto (Enterolobium cyclorobium),” Jurnal Hutan Tropis, vol. 2, no. 1, pp. 1–19, 2019.
M. Kurniawan, S. Junus, and R. Sidhartawan, “Pengaruh Volume Fraksi Perekat terhadap Kekuatan Bending Komposit Partikel Kayu Sengon dengan Metode Hot Press,” Jurnal Stator, vol. Vol. 1, p. No. 1, hal. 67–70, 2018.
D. Roza, M. Dirhamsyah, and Nurhaida, “SIFAT FISIK DAN MEKANIK PAPAN PARTIKELDARI KAYU SENGON (PARASERIANTHES FALCATARIA. L) DAN SERBUK SABUT KELAPA (COCOS NUCIFERA.L) Physical and Mechanical Properties of Particle Board from Sengon Wood (Paraserianthes falcataria. L) and Coconut Powder (Cocos,” Hutan Lestari, vol. 3, no. 3, pp. 374–382, 2015.
V. Reza et al., “Pemanfaatan Serbuk Gergaji Kayu Jati (Tectona Grandis L>F) Sebagai Adsorber Logam CU (II),” Bussiness Law binus, vol. 7, no. 2, pp. 33–48, 2020.
H. Maknunin and M. Santoso, “Pemanfaatan Limbah Rumput Laut sebagai Media Campuran terhadap Pertumbuhan dan Produktivitas Jamur Tiram Putih (Pleurotus ostreatus),” Jurnal Produksi Tanaman, vol. 8, no. 1, pp. 23–30, 2020.
N. A. Kurniawan, F. Setiawan, and E. Sofyan, “Pengujian Tarik Komposit Spesimen Campuran Serat Pisang Alur Diagonal Dan Pasir Besi Dengan Matrik Resin Polyester Dengan Metode Hand Lay-Up,” Teknika STTKD: Jurnal Teknik, Elektronik, Engine, vol. 8, no. 2, pp. 281–288, 2022, doi: 10.56521/teknika.v8i2.657.
A. Hidayat, H. Yudo, and P. Manik, “Analisa Teknis Komposit Sandwich Berpenguat Serat Daun Nanas Dengan Core Serbuk Gergaji Kayu Sengon Laut Ditinjau dari Kekuatan Tekuk dan Impak,” Jurnal Teknik Perkapalan, vol. 4, no. 1, pp. 265–273, 2016.
R. Widyorini and P. A. Nugraha, “Sifat Fisis dan Mekanis Papan Partikel Sengon dengan Perekat Asam Sitrat-Sukrosa (Physical and Mechanical Properties of Sengon Particleboard Using Citric Acid-Sucrose Adhesive),” Ilmu Teknologi Kayu Tropis, vol. 13, no. 2, pp. 175–184, 2015.
Sunardi, M. Fawaid, R. Lusiani, and R. Parulian, “Pengaruh Butiran Filler Kayu Sengon terhadap Karakteristik Papan Partikel yang Berpenguat Serat Tandan Kosong Kelapa Sawit,” Jurnal Mesin Teknologi (SINTEK Jurnal, vol. 11, no. 1, pp. 28–32, 2017.
P. F. L. Nielsen, “Pemanfaatan cabang dengan kulit kayu sengon (,” jurnal bumi lestari, vol. 10, no. 1, pp. 75–81, 2010.